The sulfite process produces wood pulp which is almost pure cellulose fibers by using various salts of sulfurous acid to extract the lignin from wood chips in large pressure vessels called digesters. The salts used in the pulping process are either sulfites (SO32−), or bisulfites (HSO3−), depending on the pH. The counter ion can be sodium (Na+), calcium (Ca2+), potassium (K+), magnesium (Mg2+) or ammonium (NH4+).
- 1 History
- 2 Processes involved in sulfite pulping
- 3 Applications
- 4 Byproducts
- 5 See also
- 6 References
The use of wood to make pulp for paper began with the development of mechanical pulping in Germany by F.G. Keller in the 1840s. Chemical processes quickly followed, first with J. Roth's use of sulfurous acid to treat wood, followed by Benjamin Chew Tilghman's US patent on the use of calcium bisulfite, Ca(HSO3)2, to pulp wood in 1867. Almost a decade later in 1874 the first commercial sulfite process|sulfite pulp mill was built in Sweden. It used magnesium as the counter ion and was based on work by Carl Daniel Ekman.
By 1900 sulfite pulping had become the dominant means of producing wood pulp, surpassing mechanical pulping methods. The competing chemical pulping process, the sulfate or kraft process was developed by Carl F. Dahl in 1879 and the first kraft mill started (in Sweden) in 1890. The first sulphite mill in the United States was the Richmond Paper Company in Rumford, Rhode Island in the mid-1880s. The invention of the recovery boiler by G.H. Tomlinson in the early 1930s  allowed kraft mills to recycle almost all of their pulping chemicals. This, along with the ability of the kraft process to accept a wider variety of types of wood and produce stronger fibers  made the kraft process the dominant pulping process starting in the 1940s. Sulfite pulps now account for less than 10% of the total chemical pulp production and the number of sulfite mills continues to decrease.
Magnesium was the standard counter ion until calcium replaced it in the 1950s.
Processes involved in sulfite pulping
Pulping liquor preparation
- S + O2 → SO2
- SO2 + H2O ⇌ H2SO3
- 2 SO2 + O2 → 2SO3
- SO3 + H2O ⇌ H2SO4
Sulfuric acid is undesirable since it promotes hydrolysis of cellulose without contributing to delignification.
The cooking liquor is prepared by adding the counter ions as hydroxides or carbonates. The relative amounts of each species present in the liquid depend largely on the relative amounts of sulfurous used. For monovalent (Na+, K+ and NH4+) hydroxides, MOH:
- H2SO3 + MOH → MHSO3 + H2O
- MHSO3 + MOH → M2SO3 + H2O
For divalent (Ca2+, Mg2+) carbonates, MCO3:
- MCO3 + 2H2SO3 → M(HSO3)2 + CO2 + H2O
- M(HSO3)2 + MCO3 → 2 MSO3 + CO2 + H2O
Sulfite pulping is carried out between pH 1.5 and 5, depending on the counterion to sulfite (bisulfite) and the ratio of base to sulfurous acid. The pulp is in contact with the pulping chemicals for 4 to 14 hours and at temperatures ranging from 130 to 160 °C (266 to 320 °F), again depending on the chemicals used.
Most of the intermediates involved in delignification in sulfite pulping are resonance-stabilized carbocations formed either by protonation of carbon-carbon double bonds or acidic cleavage of ether bonds which connect many of the constituents of lignin. It is the latter reaction which is responsible for most lignin degradation in the sulfite process. The electrophilic carbocations react with bisulfite ions (HSO3−)to give sulfonates.
- R-O-R' + H+ → R+ + R'OH
- R+ + HSO3− → R-SO3H
The spent cooking liquor from sulfite pulping is usually called brown liquor, but the terms red liquor, thick liquor and sulfite liquor are also used (compared to black liquor in the kraft process). Pulp washers, using countercurrent flow, remove the spent cooking chemicals and degraded lignin and hemicellulose. The extracted brown liquor is concentrated, in multiple effect evaporators. The concentrated brown liquor can be burned in the recovery boiler to generate steam and recover the inorganic chemicals for reuse in the pulping process or it can be neutralized to recover the useful byproducts of pulping. Recent developments in Chemrec's black liquor gasification process, adapting the technology to use in the sulfite pulping process, could make second generation biofuels production an alternative to the conventional recovery boiler technology.
The earliest process used calcium, obtained as inexpensive calcium carbonate and there was little incentive to recover the inorganic materials.
The recovery process used in magnesium-based sulfite pulping the "Magnefite" process is well developed. The concentrated brown liquor is burned in a recovery boiler, producing magnesium oxide and sulfur dioxide, both of which are recovered from the flue gases. Magnesium oxide is recovered in a wet scrubber to give a slurry of magnesium hydroxide.
- MgO + H2O → Mg(OH)2
This magnesium hydroxide slurry is then used in another scrubber to absorb sulfur dioxide from the flue gases producing a magnesium bisulfite solution that is clarified, filtered and used as the pulping liquor.
- Mg(OH)2 + 2 SO2 → Mg(HSO3)2
Sodium-based processes use a recovery system similar to that used in the kraft recovery process, except that there is no "lime cycle".
Fort William Pulp Mill
The Fort William Pulp Mill, at Corpach in Invernessshire, used the sulphite process to produce pulp. The residue of the process was called 'green liquor' and this was used as fuel in the recovery boilers. The burning of the fuel heated water to steam for use in the pulp and the paper mill. The burning of the green liquor produced hot molten sodium that was collected in the bottom of the boiler. Some 38 of this type of boiler had been built throughout the world at the time that the pulp mill was closed. Of these 32 had catastrophic explosions when the steam pipes ruptured and water cascaded onto the hot liquid sodium at the bottom of the boiler. The two boilers at Fort William were fitted with blast walls that faced towards the Argyll hills and away from Corpach. The risk of the water pipes failing was well known and the engineers kept a keen watch on the state of the steam pipes. The mill was closed for commercial reasons and not safety. In hindsight the reason for closure was based on mis-information
The sulfite process is acidic and one of the drawbacks is that the acidic conditions hydrolyze some of the cellulose, which means that sulfite pulp fibers are not as strong as kraft pulp fibers. The yield of pulp (based on wood used) is higher than for kraft pulping and sulfite pulp is easier to bleach.
Sulfite pulp remains an important commodity, especially for specialty papers and as a source of cellulose for non-paper applications. It is used to make fine paper, tissue, glassine. and to add strength to newsprint.
A special grade of bleached sulfite pulp is known as dissolving pulp which is the raw material for a wide variety of cellulose derivatives, for example rayon, cellophane, cellulose acetate and methylcellulose.
Rayon is a reconstituted cellulose fiber used to make many fabrics.
Cellophane is a clear reconstituted cellulose film used in wrapping and windows in envelopes.
Cellulose acetate was used to make flexible films for photographic use, computer tapes and so on and also to make fibers.
Sulfite pulping is generally less destructive than kraft pulping, so there are more usable byproducts.
Chief among sulfite process byproducts are lignosulfonates, which find a wide variety of uses whereas relatively inexpensive agent is needed to make a water dispersion of a water-insoluble material. Lignosulfonates are used in tanning leather, making concrete, drilling mud, drywall and so on.
Oxidation of lignosulfonates was used to produce vanillin (artificial vanilla), and this process is still used by one supplier (Borregaard, Norway) while all North American production by this route ceased in the 1990s.
- E. Sjöström (1993). Wood Chemistry: Fundamentals and Applications. Academic Press. ISBN 0-12-647480-X.
- Biermann, Christopher J. (1993). Essentials of Pulping and Papermaking. San Diego: Academic Press, Inc. ISBN 0-12-097360-X.
- "History of Paper". Retrieved 2007-10-08.
- "Swedish, German mills phase out sulfite". Pulp and Paper. January 1997. Retrieved 2007-10-08.
- "Wisconsin sulfite mill shuts down 2005". Retrieved 2007-10-07.
- Friederich, Steven (September 25, 2006). "Living on borrowed time its whole life (Weyerhauser sulfite mill)". The Daily World. Retrieved 2007-10-08.[dead link]
- Chemrec web site
- "Magnefite process". Retrieved 2007-10-11.
- "Grades and uses of paper". Retrieved 2007-10-12.
- "Dissolving pulp by the sulfite process". Retrieved 2007-10-12.
- "Applications for Methocel cellulose ethers from Dow Chemical". Retrieved 2007-10-12.
- "Uses of lignosulfonates". Retrieved 2007-10-07.
- Hocking, Martin B. (September 1997). "Vanillin: Synthetic Flavoring from Spent Sulfite Liquor" (PDF). Journal of Chemical Education 74 (9): 1055. Bibcode:1997JChEd..74.1055H. doi:10.1021/ed074p1055. Retrieved 2006-09-09.