Bulk modulus

Illustration of uniform compression

The bulk modulus ($K$ or $B$) of a substance measures the substance's resistance to uniform compression. It is defined as the ratio of the infinitesimal pressure increase to the resulting relative decrease of the volume. Its SI unit is the pascal, and its dimensional form is M¹L⁻¹T⁻².

Definition

The bulk modulus $K>0$ can be formally defined by the equation

$K=-V{\frac {\mathrm {d} P}{\mathrm {d} V}}$

where $P$ is pressure, $V$ is volume, and $dP/dV$ denotes the derivative of pressure with respect to volume. Equivalently

$K=\rho {\frac {\mathrm {d} P}{\mathrm {d} \rho }}$

where ρ is density and dP/dρ denotes the derivative of pressure with respect to density. The inverse of the bulk modulus gives a substance's compressibility.

Other moduli describe the material's response (strain) to other kinds of stress: the shear modulus describes the response to shear, and Young's modulus describes the response to linear stress. For a fluid, only the bulk modulus is meaningful. For an anisotropic solid such as wood or paper, these three moduli do not contain enough information to describe its behaviour, and one must use the full generalized Hooke's law.

Thermodynamic relation

Strictly speaking, the bulk modulus is a thermodynamic quantity, and in order to specify a bulk modulus it is necessary to specify how the temperature varies during compression: constant-temperature (isothermal $K_{T}$), constant-entropy (adiabatic $K_{S}$), and other variations are possible. Such distinctions are especially relevant for gases.

For an ideal gas, the adiabatic bulk modulus $K_{S}$ is given by

$K_{S}=\gamma \,P$

and the isothermal bulk modulus $K_{T}$ is given by

$K_{T}=P\,$

where

γ is the adiabatic index, sometimes called κ.

P is the pressure.

When the gas is not ideal, these equations give only an approximation of the bulk modulus. In a fluid, the bulk modulus K and the density ρ determine the speed of sound c (pressure waves), according to the Newton-Laplace formula

$c={\sqrt {\frac {K}{\rho }}}.$

In solids, $K_{S}$ and $K_{T}$ have very similar values. Solids can also sustain transverse waves: for these materials one additional elastic modulus, for example the shear modulus, is needed to determine wave speeds.

Measurement

It is possible to measure the bulk modulus using powder diffraction under applied pressure. It is a property of a fluid which shows its ability to change its volume under its pressure.

Selected values

Approximate bulk modulus (K) for common materials

Material	Bulk modulus in GPa	Bulk modulus in psi
Glass (see also diagram below table)	35 to 55	5.8×106
Steel	160	23×106
Diamond (at 4K)	443	64×106

Influences of selected glass component additions on the bulk modulus of a specific base glass.

A material with a bulk modulus of 35 GPa loses one percent of its volume when subjected to an external pressure of 0.35 GPa (~3500 Bar).

Approximate bulk modulus (K) for other substances

Water	2.2×109 Pa (value increases at higher pressures)
Methanol	8.23×108 Pa (at 20 °C and 1 Atm)
Air	1.42×105 Pa (adiabatic bulk modulus)
Air	1.01×105 Pa (constant temperature bulk modulus)
Solid helium	5×107 Pa (approximate)

References

Conversion formulae
Homogeneous isotropic linear elastic materials have their elastic properties uniquely determined by any two moduli among these; thus, given any two, any other of the elastic moduli can be calculated according to these formulas, provided both for 3D materials (first part of the table) and for 2D materials (second part).
3D formulae	$K=\,$	$E=\,$	$\lambda =\,$	$G=\,$	$\nu =\,$	$M=\,$	Notes
$(K,\,E)$			${\tfrac {3K(3K-E)}{9K-E}}$	${\tfrac {3KE}{9K-E}}$	${\tfrac {3K-E}{6K}}$	${\tfrac {3K(3K+E)}{9K-E}}$
$(K,\,\lambda )$		${\tfrac {9K(K-\lambda )}{3K-\lambda }}$		${\tfrac {3(K-\lambda )}{2}}$	${\tfrac {\lambda }{3K-\lambda }}$	$3K-2\lambda \,$
$(K,\,G)$		${\tfrac {9KG}{3K+G}}$	$K-{\tfrac {2G}{3}}$		${\tfrac {3K-2G}{2(3K+G)}}$	$K+{\tfrac {4G}{3}}$
$(K,\,\nu )$		$3K(1-2\nu )\,$	${\tfrac {3K\nu }{1+\nu }}$	${\tfrac {3K(1-2\nu )}{2(1+\nu )}}$		${\tfrac {3K(1-\nu )}{1+\nu }}$
$(K,\,M)$		${\tfrac {9K(M-K)}{3K+M}}$	${\tfrac {3K-M}{2}}$	${\tfrac {3(M-K)}{4}}$	${\tfrac {3K-M}{3K+M}}$
$(E,\,\lambda )$	${\tfrac {E+3\lambda +R}{6}}$			${\tfrac {E-3\lambda +R}{4}}$	${\tfrac {2\lambda }{E+\lambda +R}}$	${\tfrac {E-\lambda +R}{2}}$	$R={\sqrt {E^{2}+9\lambda ^{2}+2E\lambda }}$
$(E,\,G)$	${\tfrac {EG}{3(3G-E)}}$		${\tfrac {G(E-2G)}{3G-E}}$		${\tfrac {E}{2G}}-1$	${\tfrac {G(4G-E)}{3G-E}}$
$(E,\,\nu )$	${\tfrac {E}{3(1-2\nu )}}$		${\tfrac {E\nu }{(1+\nu )(1-2\nu )}}$	${\tfrac {E}{2(1+\nu )}}$		${\tfrac {E(1-\nu )}{(1+\nu )(1-2\nu )}}$
$(E,\,M)$	${\tfrac {3M-E+S}{6}}$		${\tfrac {M-E+S}{4}}$	${\tfrac {3M+E-S}{8}}$	${\tfrac {E-M+S}{4M}}$		$S=\pm {\sqrt {E^{2}+9M^{2}-10EM}}$ There are two valid solutions. The plus sign leads to $\nu \geq 0$. The minus sign leads to $\nu \leq 0$.
$(\lambda ,\,G)$	$\lambda +{\tfrac {2G}{3}}$	${\tfrac {G(3\lambda +2G)}{\lambda +G}}$			${\tfrac {\lambda }{2(\lambda +G)}}$	$\lambda +2G\,$
$(\lambda ,\,\nu )$	${\tfrac {\lambda (1+\nu )}{3\nu }}$	${\tfrac {\lambda (1+\nu )(1-2\nu )}{\nu }}$		${\tfrac {\lambda (1-2\nu )}{2\nu }}$		${\tfrac {\lambda (1-\nu )}{\nu }}$	Cannot be used when $\nu =0\Leftrightarrow \lambda =0$
$(\lambda ,\,M)$	${\tfrac {M+2\lambda }{3}}$	${\tfrac {(M-\lambda )(M+2\lambda )}{M+\lambda }}$		${\tfrac {M-\lambda }{2}}$	${\tfrac {\lambda }{M+\lambda }}$
$(G,\,\nu )$	${\tfrac {2G(1+\nu )}{3(1-2\nu )}}$	$2G(1+\nu )\,$	${\tfrac {2G\nu }{1-2\nu }}$			${\tfrac {2G(1-\nu )}{1-2\nu }}$
$(G,\,M)$	$M-{\tfrac {4G}{3}}$	${\tfrac {G(3M-4G)}{M-G}}$	$M-2G\,$		${\tfrac {M-2G}{2M-2G}}$
$(\nu ,\,M)$	${\tfrac {M(1+\nu )}{3(1-\nu )}}$	${\tfrac {M(1+\nu )(1-2\nu )}{1-\nu }}$	${\tfrac {M\nu }{1-\nu }}$	${\tfrac {M(1-2\nu )}{2(1-\nu )}}$
2D formulae	$K_{\mathrm {2D} }=\,$	$E_{\mathrm {2D} }=\,$	$\lambda _{\mathrm {2D} }=\,$	$G_{\mathrm {2D} }=\,$	$\nu _{\mathrm {2D} }=\,$	$M_{\mathrm {2D} }=\,$	Notes
$(K_{\mathrm {2D} },\,E_{\mathrm {2D} })$			${\tfrac {2K_{\mathrm {2D} }(2K_{\mathrm {2D} }-E_{\mathrm {2D} })}{4K_{\mathrm {2D} }-E_{\mathrm {2D} }}}$	${\tfrac {K_{\mathrm {2D} }E_{\mathrm {2D} }}{4K_{\mathrm {2D} }-E_{\mathrm {2D} }}}$	${\tfrac {2K_{\mathrm {2D} }-E_{\mathrm {2D} }}{2K_{\mathrm {2D} }}}$	${\tfrac {4K_{\mathrm {2D} }^{2}}{4K_{\mathrm {2D} }-E_{\mathrm {2D} }}}$
$(K_{\mathrm {2D} },\,\lambda _{\mathrm {2D} })$		${\tfrac {4K_{\mathrm {2D} }(K_{\mathrm {2D} }-\lambda _{\mathrm {2D} })}{2K_{\mathrm {2D} }-\lambda _{\mathrm {2D} }}}$		$K_{\mathrm {2D} }-\lambda _{\mathrm {2D} }$	${\tfrac {\lambda _{\mathrm {2D} }}{2K_{\mathrm {2D} }-\lambda _{\mathrm {2D} }}}$	$2K_{\mathrm {2D} }-\lambda _{\mathrm {2D} }$
$(K_{\mathrm {2D} },\,G_{\mathrm {2D} })$		${\tfrac {4K_{\mathrm {2D} }G_{\mathrm {2D} }}{K_{\mathrm {2D} }+G_{\mathrm {2D} }}}$	$K_{\mathrm {2D} }-G_{\mathrm {2D} }$		${\tfrac {K_{\mathrm {2D} }-G_{\mathrm {2D} }}{K_{\mathrm {2D} }+G_{\mathrm {2D} }}}$	$K_{\mathrm {2D} }+G_{\mathrm {2D} }$
$(K_{\mathrm {2D} },\,\nu _{\mathrm {2D} })$		$2K_{\mathrm {2D} }(1-\nu _{\mathrm {2D} })\,$	${\tfrac {2K_{\mathrm {2D} }\nu _{\mathrm {2D} }}{1+\nu _{\mathrm {2D} }}}$	${\tfrac {K_{\mathrm {2D} }(1-\nu _{\mathrm {2D} })}{1+\nu _{\mathrm {2D} }}}$		${\tfrac {2K_{\mathrm {2D} }}{1+\nu _{\mathrm {2D} }}}$
$(E_{\mathrm {2D} },\,G_{\mathrm {2D} })$	${\tfrac {E_{\mathrm {2D} }G_{\mathrm {2D} }}{4G_{\mathrm {2D} }-E_{\mathrm {2D} }}}$		${\tfrac {2G_{\mathrm {2D} }(E_{\mathrm {2D} }-2G_{\mathrm {2D} })}{4G_{\mathrm {2D} }-E_{\mathrm {2D} }}}$		${\tfrac {E_{\mathrm {2D} }}{2G_{\mathrm {2D} }}}-1$	${\tfrac {4G_{\mathrm {2D} }^{2}}{4G_{\mathrm {2D} }-E_{\mathrm {2D} }}}$
$(E_{\mathrm {2D} },\,\nu _{\mathrm {2D} })$	${\tfrac {E_{\mathrm {2D} }}{2(1-\nu _{\mathrm {2D} })}}$		${\tfrac {E_{\mathrm {2D} }\nu _{\mathrm {2D} }}{(1+\nu _{\mathrm {2D} })(1-\nu _{\mathrm {2D} })}}$	${\tfrac {E_{\mathrm {2D} }}{2(1+\nu _{\mathrm {2D} })}}$		${\tfrac {E_{\mathrm {2D} }}{(1+\nu _{\mathrm {2D} })(1-\nu _{\mathrm {2D} })}}$
$(\lambda _{\mathrm {2D} },\,G_{\mathrm {2D} })$	$\lambda _{\mathrm {2D} }+G_{\mathrm {2D} }$	${\tfrac {4G_{\mathrm {2D} }(\lambda _{\mathrm {2D} }+G_{\mathrm {2D} })}{\lambda _{\mathrm {2D} }+2G_{\mathrm {2D} }}}$			${\tfrac {\lambda _{\mathrm {2D} }}{\lambda _{\mathrm {2D} }+2G_{\mathrm {2D} }}}$	$\lambda _{\mathrm {2D} }+2G_{\mathrm {2D} }\,$
$(\lambda _{\mathrm {2D} },\,\nu _{\mathrm {2D} })$	${\tfrac {\lambda _{\mathrm {2D} }(1+\nu _{\mathrm {2D} })}{2\nu _{\mathrm {2D} }}}$	${\tfrac {\lambda _{\mathrm {2D} }(1+\nu _{\mathrm {2D} })(1-\nu _{\mathrm {2D} })}{\nu _{\mathrm {2D} }}}$		${\tfrac {\lambda _{\mathrm {2D} }(1-\nu _{\mathrm {2D} })}{2\nu _{\mathrm {2D} }}}$		${\tfrac {\lambda _{\mathrm {2D} }}{\nu _{\mathrm {2D} }}}$	Cannot be used when $\nu _{\mathrm {2D} }=0\Leftrightarrow \lambda _{\mathrm {2D} }=0$
$(G_{\mathrm {2D} },\,\nu _{\mathrm {2D} })$	${\tfrac {G_{\mathrm {2D} }(1+\nu _{\mathrm {2D} })}{1-\nu _{\mathrm {2D} }}}$	$2G_{\mathrm {2D} }(1+\nu _{\mathrm {2D} })\,$	${\tfrac {2G_{\mathrm {2D} }\nu _{\mathrm {2D} }}{1-\nu _{\mathrm {2D} }}}$			${\tfrac {2G_{\mathrm {2D} }}{1-\nu _{\mathrm {2D} }}}$
$(G_{\mathrm {2D} },\,M_{\mathrm {2D} })$	$M_{\mathrm {2D} }-G_{\mathrm {2D} }$	${\tfrac {4G_{\mathrm {2D} }(M_{\mathrm {2D} }-G_{\mathrm {2D} })}{M_{\mathrm {2D} }}}$	$M_{\mathrm {2D} }-2G_{\mathrm {2D} }\,$		${\tfrac {M_{\mathrm {2D} }-2G_{\mathrm {2D} }}{M_{\mathrm {2D} }}}$