Compression set

The compression set (ASTM D395) of a material is the permanent deformation remaining after removal of a force that was applied to it. The term is normally applied to soft materials such as elastomers. Compression is normally measured in two ways: compression set A and compression set B.^[1]

Compression Set A

This has the formal name compression set under constant force in air. In compression set A a force of 1.8 kN is applied to the specimen for a set time at a set temperature. Compression set A is defined as the percentage of original specimen thickness after the specimen has been left in normal conditions for 30 minutes. C_A, the compression set A is given by C_A = [(t_o - t_i) / t_o] * 100 where t_o is the original specimen thickness and t_i is the specimen thickness after testing.^[1]

Compression Set B

This has the formal name compression set under constant deflection in air. The specimen is compressed to 75% of its original height for a set time and at a set temperature (sample is compressed to .75 of its original height) Compression set B is (like Compression set A) defined as the percentage of original specimen thickness after it has been left in normal conditions for 30 minutes. C_B, the compression set B is given by C_B = [(t_o - t_i) / (t_o - t_n)] * 100 where t_o is the original specimen thickness, t_i is the specimen thickness after testing and t_n is the spacer thickness or the specimen thickness during the test.^[1]

References

^ ^a ^b ^c "Compression Set - ASTM D395 Plastic Test Standard". IDES. Integrated Design Engineering Systems. Archived from the original on 28 December 2011. Retrieved 15 June 2012.

This material-related article is a stub. You can help Wikipedia by expanding it.