Constantan: Difference between revisions
No edit summary |
Added Eureka name |
||
| Line 1: | Line 1: | ||
'''Constantan''' is a [[copper]]-[[nickel]] [[alloy]] usually consisting of 55% copper and 45% nickel.<ref name=Davis158>Davis, p.158.</ref> |
'''Constantan''' is a [[copper]]-[[nickel]] [[alloy]] usually consisting of 55% copper and 45% nickel.<ref name=Davis158>Davis, p.158.</ref> |
||
Its main feature is its [[resistivity]] which is constant over a wide range of temperatures. Other alloys with similarly low [[temperature coefficient]]s are known, such as [[manganin]] (Cu<sub>86</sub>Mn<sub>12</sub>Ni<sub>2</sub>). |
Its main feature is its [[resistivity]] which is constant over a wide range of temperatures. Other alloys with similarly low [[temperature coefficient]]s are known, such as [[manganin]] (Cu<sub>86</sub>Mn<sub>12</sub>Ni<sub>2</sub>). |
||
An alternate trade name is Eureka http://www.resistancewires.co.uk/products_RW45_Eureka.html |
|||
== History == |
== History == |
||
Revision as of 10:04, 13 June 2010
Constantan is a copper-nickel alloy usually consisting of 55% copper and 45% nickel.[1] Its main feature is its resistivity which is constant over a wide range of temperatures. Other alloys with similarly low temperature coefficients are known, such as manganin (Cu86Mn12Ni2).
An alternate trade name is Eureka http://www.resistancewires.co.uk/products_RW45_Eureka.html
History
In 1887 Edward Weston discovered that metals can have a negative temperature coefficient of resistance, inventing what he called his "Alloy No. 2." It was produced in Germany where it was renamed "constantan". [2] [3]
Constantan alloy
Of all modern strain gauge alloys, constantan is the oldest, and still the most widely used. This situation reflects the fact that constantan has the best overall combination of properties needed for many strain gauge applications. This alloy has, for example, an adequately high strain sensitivity, or gauge factor, which is relatively insensitive to strain level and temperature. Its resistivity is high enough to achieve suitable resistance values in even very small grids, and its temperature coefficient of resistance is not excessive. In addition, constantan is characterized by good fatigue life and relatively high elongation capability. It must be noted, however, that constantan tends to exhibit a continuous drift at temperatures above 65 °C (150 °F); and this characteristic should be taken into account when zero stability of the strain gauge is critical over a period of hours or days.
A-Alloy
Very importantly, constantan can be processed for self-temperature compensation to match a wide range of test material coefficients of thermal expansion. An alloy is supplied in self-temperature-compensation (S-T-C) numbers 00, 03, 05, 06, 09, 13, 15, 18, 30, 40 and 50, for use on test materials with corresponding thermal expansion coefficients, expressed in parts per million by length (or µm/m) per kelvin or degree Celsius or degree Fahrenheit.
P alloy
For the measurement of very large strains, 5% (50 000 microstrain) or above, annealed constantan (P alloy) is the grid material normally selected. Constantan in this form is very ductile; and, in gauge lengths of 0.125 in (3 mm) and longer, can be strained to >20%. It should be borne in mind, however, that under high cyclic strains the P alloy will exhibit some permanent resistivity change with each cycle, and cause a corresponding zero shift in the strain gauge. Because of this characteristic, and the tendency for premature grid failure with repeated straining, P alloy is not ordinarily recommended for cyclic strain applications. P alloy is available with S-T-C numbers of 08 and 40 for use on metals and plastics, respectively.
Physical properties
| Electrical resistivity at room temperature[1] | 500 nΩ·m |
| Temperature coefficient at 20 °C[4] | 8 ppm/K-1 |
| Temperature coefficient -55 to 105 °C[1] | ±40 ppm/K-1 |
| Density[1] | 8.9 × 103 kg/m³ |
| Melting point | 1221 to 1300 °C |
| Specific heat capacity | 0.39 J/(g·K) |
| Thermal conductivity at 23°C | 19.5 W/(m.K) |
| Linear coefficient of thermal expansion at 25-105°C [1] | 14.9 × 10-6 K-1 |
| Tensile strength[1] | 455-860 MPa |
| Elongation at fracture | <45% |
| Elastic modulus | 162 GPa |
Temperature Measurement
Constantan is also used to form thermocouples with wires made of iron, copper, or chromel.
References
- ^ a b c d e f Davis, p.158.
- ^ A chronological history of electrical development from 600 B.C., p.59, National Electrical Manufacturers Association, 1946.
- ^ David Oakes Woodbury A measure for greatness: a short biography of Edward Weston, p.168, McGraw-Hill, 1949.
- ^ John O'Malley, Schaum's outline of theory and problems of basic circuit analysis, p.19, McGraw-Hill Professional, 1992 ISBN 0070478244
Bibliography
- Joseph R. Davis, Copper and copper alloys, ASM International, 2001 ISBN 0871707268.