High-strength low-alloy steel

From Wikipedia, the free encyclopedia

This is an old revision of this page, as edited by The joy of all things (talk | contribs) at 16:27, 14 November 2023 (→Advantages of HSLA Steel:: As per WP:WCW, "One heading in this article ends with a colon "== Heading : ==". This colon can be deleted."). The present address (URL) is a permanent link to this revision, which may differ significantly from the current revision.

Steels
Phases
Microstructures
Classes
Other iron-based materials

High-strength low-alloy steel (HSLA) is a type of alloy steel that provides better mechanical properties or greater resistance to corrosion than carbon steel. HSLA steels vary from other steels in that they are not made to meet a specific chemical composition but rather specific mechanical properties. They have a carbon content between 0.05 and 0.25% to retain formability and weldability. Other alloying elements include up to 2.0% manganese and small quantities of copper, nickel, niobium, nitrogen, vanadium, chromium, molybdenum, titanium, calcium, rare-earth elements, or zirconium.[1][2] Copper, titanium, vanadium, and niobium are added for strengthening purposes.[2] These elements are intended to alter the microstructure of carbon steels, which is usually a ferrite-pearlite aggregate, to produce a very fine dispersion of alloy carbides in an almost pure ferrite matrix. This eliminates the toughness-reducing effect of a pearlitic volume fraction yet maintains and increases the material's strength by refining the grain size, which in the case of ferrite increases yield strength by 50% for every halving of the mean grain diameter. Precipitation strengthening plays a minor role, too. Their yield strengths can be anywhere between 250–590 megapascals (36,000–86,000 psi). Because of their higher strength and toughness HSLA steels usually require 25 to 30% more power to form, as compared to carbon steels.[2]

Copper, silicon, nickel, chromium, and phosphorus are added to increase corrosion resistance. Zirconium, calcium, and rare-earth elements are added for sulfide-inclusion shape control which increases formability. These are needed because most HSLA steels have directionally sensitive properties. Formability and impact strength can vary significantly when tested longitudinally and transversely to the grain. Bends that are parallel to the longitudinal grain are more likely to crack around the outer edge because it experiences tensile loads. This directional characteristic is substantially reduced in HSLA steels that have been treated for sulfide shape control.[2]

They are used in cars, trucks, cranes, bridges, roller coasters and other structures that are designed to handle large amounts of stress or need a good strength-to-weight ratio.[2] HSLA steel cross-sections and structures are usually 20 to 30% lighter than a carbon steel with the same strength.[3][4]

HSLA steels are also more resistant to rust than most carbon steels because of their lack of pearlite – the fine layers of ferrite (almost pure iron) and cementite in pearlite.[5] HSLA steels usually have densities of around 7800 kg/m3.[6]

Military armour plate is mostly made from alloy steels, although some civilian armour against small arms is now made from HSLA steels with extreme low temperature quenching.[7]

Classifications

  • Weathering steels: Steels which have better corrosion resistance. A common example is COR-TEN.
  • Control-rolled steels: Hot rolled steels which have a highly deformed austenite structure that will transform to a very fine equiaxed ferrite structure upon cooling.
  • Pearlite-reduced steels: Low carbon content steels which lead to little or no pearlite, but rather a very fine grain ferrite matrix. It is strengthened by precipitation hardening.
  • Acicular ferrite steels: These steels are characterized by a very fine high strength acicular ferrite structure, a very low carbon content, and good hardenability.
  • Dual-phase steels: These steels have a ferrite microstructure that contain small, uniformly distributed sections of martensite. This microstructure gives the steels a low yield strength, high rate of work hardening, and good formability.[1]
  • Microalloyed steels: Steels which contain very small additions of niobium, vanadium, and/or titanium to obtain a refined grain size and/or precipitation hardening.

A common type of micro-alloyed steel is improved-formability HSLA. It has a yield strength up to 80,000 psi (550 MPa) but costs only 24% more than A36 steel (36,000 psi (250 MPa)). One of the disadvantages of this steel is that it is 30 to 40% less ductile. In the U.S., these steels are dictated by the ASTM standards A1008/A1008M and A1011/A1011M for sheet metal and A656/A656M for plates. These steels were developed for the automotive industry to reduce weight without losing strength. Examples of uses include door-intrusion beams, chassis members, reinforcing and mounting brackets, steering and suspension parts, bumpers, and wheels.[2][8]

Advantages of HSLA Steel

Superior Strength: HSLA plates provide exceptional strength, making them perfect for heavy-duty applications. At the same time, they reduce the overall weight of structures or machinery.

Cost-Effective: Despite their enhanced properties, HSLA plates are cost-effective due to their reduced material usage and extended service life.

Corrosion Resistance: These plates are designed to resist corrosion, ensuring a longer lifespan even in harsh environments.

Enhanced Weldability: HSLA plates are easier to weld, enabling efficient fabrication and construction processes.

Versatility: With the ability to be customized to various sizes and dimensions, HSLA plates find versatile applications in diverse industries.[9]

SAE grades

The Society of Automotive Engineers (SAE) maintains standards for HSLA steel grades because they are often used in automotive applications.

SAE HSLA steel grade compositions[10]
Grade % Carbon (max) % Manganese (max) % Phosphorus (max) % Sulfur (max) % Silicon (max) Notes
942X 0.21 1.35 0.04 0.05 0.90 Niobium or vanadium treated
945A 0.15 1.00 0.04 0.05 0.90
945C 0.23 1.40 0.04 0.05 0.90
945X 0.22 1.35 0.04 0.05 0.90 Niobium or vanadium treated
950A 0.15 1.30 0.04 0.05 0.90
950B 0.22 1.30 0.04 0.05 0.90
950C 0.25 1.60 0.04 0.05 0.90
950D 0.15 1.00 0.15 0.05 0.90
950X 0.23 1.35 0.04 0.05 0.90 Niobium or vanadium treated
955X 0.25 1.35 0.04 0.05 0.90 Niobium, vanadium, or nitrogen treated
960X 0.26 1.45 0.04 0.05 0.90 Niobium, vanadium, or nitrogen treated
965X 0.26 1.45 0.04 0.05 0.90 Niobium, vanadium, or nitrogen treated
970X 0.26 1.65 0.04 0.05 0.90 Niobium, vanadium, or nitrogen treated
980X 0.26 1.65 0.04 0.05 0.90 Niobium, vanadium, or nitrogen treated
SAE HSLA steel grade mechanical properties[11]
Grade Form Yield strength (min) [psi (MPa)] Ultimate tensile strength (min) [psi (MPa)]
942X Plates, shapes & bars up to 4 in. 42,000 (290) 60,000 (414)
945A, C Sheet & strip 45,000 (310) 60,000 (414)
Plates, shapes & bars:
0–0.5 in. 45,000 (310) 65,000 (448)
0.5–1.5 in. 42,000 (290) 62,000 (427)
1.5–3 in. 40,000 (276) 62,000 (427)
945X Sheet, strip, plates, shapes & bars up to 1.5 in. 45,000 (310) 60,000 (414)
950A, B, C, D Sheet & strip 50,000 (345) 70,000 (483)
Plates, shapes & bars:
0–0.5 in. 50,000 (345) 70,000 (483)
0.5–1.5 in. 45,000 (310) 67,000 (462)
1.5–3 in. 42,000 (290) 63,000 (434)
950X Sheet, strip, plates, shapes & bars up to 1.5 in. 50,000 (345) 65,000 (448)
955X Sheet, strip, plates, shapes & bars up to 1.5 in. 55,000 (379) 70,000 (483)
960X Sheet, strip, plates, shapes & bars up to 1.5 in. 60,000 (414) 75,000 (517)
965X Sheet, strip, plates, shapes & bars up to 0.75 in. 65,000 (448) 80,000 (552)
970X Sheet, strip, plates, shapes & bars up to 0.75 in. 70,000 (483) 85,000 (586)
980X Sheet, strip & plates up to 0.375 in. 80,000 (552) 95,000 (655)
Ranking of various properties for SAE HSLA steel grades[12]
Rank Weldability Formability Toughness
Worst 980X 980X 980X
970X 970X 970X
965X 965X 965X
960X 960X 960X
955X, 950C, 942X 955X 955X
945C 950C 945C, 950C, 942X
950B, 950X 950D 945X, 950X
945X 950B, 950X, 942X 950D
950D 945C, 945X 950B
950A 950A 950A
Best 945A 945A 945A

Controlled rolling of HSLA steels

Mechanism

Controlled rolling

Change in microstructure at different controlled-rolling stages.

Controlled rolling is a method of refining the grain of steel by introducing a large amount of nucleation sites for ferrite in the austenite matrix by rolling it at precisely controlled temperature, thereby increasing the strength of the steel. There are three main stages in controlled rolling:[13]

1) Deformation in recrystallization regions. In this stage, austenite is being recrystallized and refined, enabling refinement of ferrite grains in a later stage.

2) Deformation in non-recrystallization regions. Austenite grains are elongated by rolling. Deformation bands might present within the band as well. Elongated grain boundaries and deformation bands are all nucleation sites for ferrite.

3) Deformation in austenite-ferrite two phase region. Ferrite nucleates and austenite are further work-hardened.

Strengthening Mechanism

Control-rolled HSLA steels contain a combination of different strengthening mechanisms. The main strengthening effect comes from grain refinement (Grain boundary strengthening), in which strength increases as the grain size decreases. The other mechanisms include solid solution strengthening and precipitate hardening from micro-alloyed elements.[14][15] After the steel passes the temperature of austenite-ferrite region, it is then further strengthened by work hardening.[14][13]

Mechanical properties

Control-rolled HSLA steels usually have higher strength and toughness, as well as lower ductile-brittle transition temperature[15] and ductile fracture properties.[14] Below are some common micro-alloyed elements used to improve the mechanical properties.

Effect of micro-alloyed elements

Niobium: Nb can increase the recrystallization temperature by around 100 °C,[13] thereby extending the non-recrystallization region and slow down the grain growth. Nb can both increase the strength and toughness by precipitate strengthening and grain refinement.[15] Moreover, Nb is a strong carbide/nitride former, the Nb(C, N) formed can hinder grain growth during austenite-to-ferrite transition.[15]  

Vanadium: V can significantly increase the strength and transition temperature by precipitate strengthening.[15]

Titanium: Ti have a slight increase in strengthen via both grain refinement and precipitate strengthening.

Nb, V, and Ti are three common alloying elements in HSLA steels. They are all good carbide and nitride former,[13] where the precipitates formed can prevent grain growth by pinning grain boundary. They are also all ferrite former, which increase the transition temperature of austenite-ferrite two phase region and reduce the non-recrystallization region.[13] The reduction in non-recrystallization region induces the formation of deformation bands and activated grain boundaries, which are alternative ferrite nucleation site other than grain boundaries.[13]

Other alloying elements are mainly for solid solution strengthening including Silicon, Manganese, Chromium, Copper, and Nickel.[15]

References

  1. ^ a b "Classification of Carbon and Low-Alloy Steels". Retrieved 2008-10-06.
  2. ^ a b c d e f "HSLA Steel". 2002-11-15. Archived from the original on 2009-12-30. Retrieved 2008-10-11.
  3. ^ Degarmo, p. 116.
  4. ^ Same density as carbon steel, see next paragraph
  5. ^ Kant, Krishan; Kumar, Lalit; Verma, Kanika; Rawat, Deepak (10 April 2016). "Effects of Various Process Parameters by Tensile and Toughness Test on Weld Joint Quality of HSLA Steel during Submerged Arc Welding". International Journal of Scientific Research in Science, Engineering and Technology. 2 (2): 652–659. doi:10.32628/IJSRSET1622216 (inactive 1 August 2023).{{cite journal}}: CS1 maint: DOI inactive as of August 2023 (link)
  6. ^ "Stainless steel properties for structural automotive applications" (PDF). Euro Inox. June 2000. Archived from the original (PDF) on 2007-09-28. Retrieved 2007-08-14.
  7. ^ "Swebor Armor 500 ballistic protection steel" (PDF). Swebarmor. Archived from the original (PDF) on 2020-01-14. Retrieved 2018-05-21.
  8. ^ Cold rolled sheet steel, archived from the original on 2008-04-30, retrieved 2008-10-11
  9. ^ "Get the Best High Strength Low Alloy Steel Price for Your Projects". www.eckhardtsteel.com. Retrieved 2023-10-20.
  10. ^ Oberg, pp. 440-441.
  11. ^ Oberg, p. 441.
  12. ^ Oberg, p. 442.
  13. ^ a b c d e f Tamura, Imao (1988). Thermomechanical Processing of High-strength Low-alloy Steels. Butterworths. ISBN 978-0-408-11034-1.[page needed]
  14. ^ a b c Morrison, W. B.; Chapman, J. A. (8 July 1976). "Rosenhain Centenary Conference - 3. Materials development present and future 3.2 Controlled rolling". Philosophical Transactions of the Royal Society of London. Series A, Mathematical and Physical Sciences. 282 (1307): 289–303. doi:10.1098/rsta.1976.0119. S2CID 136154334.
  15. ^ a b c d e f Tanaka, T. (January 1981). "Controlled rolling of steel plate and strip". International Metals Reviews. 26 (1): 185–212. doi:10.1179/imtr.1981.26.1.185.

Sources

  • Degarmo, E. Paul; Black, J T.; Kohser, Ronald A. (2003), Materials and Processes in Manufacturing (9th ed.), Wiley, ISBN 0-471-65653-4.
  • Oberg, E.; et al. (1996), Machinery's Handbook (25th ed.), Industrial Press Inc