* Strengthened by solution treatment, e.g. adding 0.01% Na (in form NaF & NaCl) to the melt just before casting |
* Strengthened by solution treatment, e.g. adding 0.01% Na (in form NaF & NaCl) to the melt just before casting |
||
* Disadvantage is the presence of porosity in the cast (forms foams), which can be avoided by casting under pressure in autoclaves |
* Disadvantage is the presence of porosity in the cast (forms foams), which can be avoided by casting under pressure in autoclaves |
||
* The nature must be preserve for the sake of our future |
|||
==References== |
==References== |
||
Revision as of 01:22, 23 June 2016
 | This article may require copy editing for grammar, style, cohesion, tone, or spelling. (June 2016) |
 | This article needs additional citations for verification. (April 2012) |
Silumin is the name that is used in some countries for casting alloys based on Al–Si system. Silumin are a series of lightweight, high-strength aluminium alloys with silicon content within the range of 3–50%.[1] Casting is the primary use of aluminum-silicon alloys, but they can also be produced by rapid solidification processes and powder metallurgy. Within the Aluminum Association designation system silumins correspond to alloys of two systems: 3xx.x – Aluminum–silicon alloys also containing magnesium and/or copper, and 4xx.x – Binary aluminum–silicon alloys. Among the advantages of silumin is its high resistance to corrosion, making it useful in humid environments. The addition of silicon to aluminium also makes it less viscous when liquid, which together with its low cost (both component elements are relatively cheap to extract), makes it a very good casting alloy and a fresher metal.[2] It is also used on 3 phase motors to allow speed regulation. Another use is in rifle scope mounts and camera mounts.
Characteristics
- High castability, high fluidity, high corrosion resistance, high ductility, low specific gravity, high machinability
- Used for large castings, which are made to operate under heavy load conditions
- Under the category of non-heat-treatable alloys but can be modified by the addition of Mg & Cu, which enables it to be heat treated, e.g. AΠ4 alloys
- Strengthened by solution treatment, e.g. adding 0.01% Na (in form NaF & NaCl) to the melt just before casting
- Disadvantage is the presence of porosity in the cast (forms foams), which can be avoided by casting under pressure in autoclaves
- The nature must be preserve for the sake of our future
References
- ^ "Aluminum-Silicon Alloys". Key To Metals. Retrieved 18 April 2012.
- ^ Pezdn, J (2008). "Effect of modification with strontium on machinability of AK9 silumin" (PDF). Polish Academy of Sciences. Retrieved 13 March 2013.
the qiuck brown fox jumps over the lazy dog near the river bank. ŒĎš
 | This alloy-related article is a stub. You can help Wikipedia by expanding it. |