Courtaulds Red Scar Works Preston
53°47′04″N 2°38′43″W / 53.7845°N 2.6454°W Red Scar Works was built in 1939 by Courtaulds and produced rayon. It was located in Ribbleton Preston off Longridge Road.[1][2] The closure of the works was announced in November 1979 and the issue raised in the UK Parliament House of Commons by the constituency MP.[3] At the time of closure approximately 2600 people were employed there but there were approximately 4000 at its peak. It was the largest rayon producing site in Britain. Two main products were manufactured with one being tyre cord by a process known as CSPT - Continuous Spinning Process Tenasco. Two main denier of this product were manufactured. The other product was a general textile called Bright. A range of deniers of this were produced in a range of colours. The trade name for the coloured product was Duracol. At the time of closure, one reason given by management for the closure was the rising popularity of steel belt radial tires thus reducing demand for tyre cord.
The factory was connected by rail as a branch of what was the Preston and Longridge Railway. The plant had its own power production facility. The main raw materials brought in by rail were coal, sulfuric acid, sodium hydroxide, carbon disulfide and wood pulp.
Buildings on site
The site had its own power station which was coal burning and a boiler house and turbine room housing Parsons Peebles turbines.[4] This resulted in two cooling towers and two large power station chimneys which were very visible points on the Preston landscape.[5] The cooling towers were very close to the Preston By-pass, now part of the M6 motorway. As well as a laboratory there was a textile testing room, boiler house, turbine room, box spinning, CSPT, effluent plant, acid recovery, zinc recovery, churn room, mixing room, dialyzer house, maintenance workshop, offices, cake ageing rooms, coneing, cakewash, carbon disulfide mixing arc, steeping room, mercerizing room, condux mill passage, fume scrubbing and viscose alley containing east and west viscose ageing and storage caves[6]
Chemical processes
Rayon production was by the viscose process.[7][8][9] This started by taking Cellulose in the form of wood pulp and steeping in caustic soda solution. The caustic soda was then drained and the pulp sheets pressed to remove residual alkali. The product is sodium cellulose hydroxide at this stage. The pressings and caustic soda were recovered by dialysis in the dialyser house. The steeped wood pulp sheets were then shredded with Condux mills and the product (called alkcell short for alkaline cellulose) stored in bins at controlled temperature. After suitable ageing, carbon disulfide was added and mixed in churns in the churn room to produce an orange coloured xanthate, chemically sodium cellulose xanthate. The contents were then dropped into mixers in the mixing room and dilute caustic soda added and mixed for a length of time. This viscous liquid was then passed through granulators to grind up the chunks of xanthate. This viscous liquid - viscose - was then filtered, deaerated, and passed into storage tanks in the viscose caves in controlled temperature and ageing conditions. The next stage is spinning of the yarn. In spinning, whether box spinning or CSPT, the principle is the same. Viscose is extruded through a spinneret (polymers) into a batch of hot dilute acid also containing sodium sulphate and zinc sulphate along with other additives. Rayon was produced and loaded onto cakes of yarn or bobbins in the case of CSPT. In the case of Duracol, pigment was injected into the viscose just before spinning, creating a dye-fast yarn.
The hot spent dilute acid from the spin baths was sent for recycling in the acid recovery building. Other waste acidic streams were sent to the zinc recovery building where the liquors were passed into tanks containing ion-exchange resin. The recycled product was an acid stream rich in zinc sulfate which was fed back into the hot dilute acid baths by means of weirs. Cakes of yarn were aged in controlled heat and humidity ageing cabinets and then sent through the cakewash process. This consisted of prewashes and then washing with sodium sulfide solution. A rinse then bleach wash followed by another very dilute acid wash and finally rinsing was then performed. The yarn was then dried in tunnel drier ovens. After this the yarn was sent to coning where the yarn was threaded onto cones for ease of handling and sale.
See also
References
- ^ "Made in Preston - Courtaulds Man Made Fibres". www.madeinpreston.co.uk.
- ^ "Britain From Above". britainfromabove.org.uk. Retrieved 2018-09-05.
- ^ "COURTAULDS, PRESTON (MILL CLOSURE) (Hansard, 28 November 1979)". api.parliament.uk. Retrieved 2018-09-05.
- ^ "Generators". Parsons Peebles. Retrieved 2018-12-05.
- ^ "Flickr Photos Courtaulds Red Scar Works".
- ^ cunliffe, gary (2014-05-14), Courtaulds In Preston, retrieved 2019-01-22
- ^ "Viscose Manufacturing Process | Part 02". Textile Study Center. Retrieved 2018-09-06.
- ^ "Viscose CV - Introduction". www.swicofil.com. Retrieved 2018-09-06.
- ^ "Flow Chart of Viscose Rayon Manufacturing Process". www.textileflowchart.com. Retrieved 2018-09-06.